Calcium Aluminate Cement, High Aluminate Cement A600, A700.G9, CA-70, CA-80

Wehewehe pōkole

ʻO ka porosity haʻahaʻa, ke kūpaʻa kemika kiʻekiʻe, ka hana wela kiʻekiʻe, ke kūpaʻa ʻaʻahu kiʻekiʻe

E HOAKAKA ANO

Nā hiʻohiʻona

ʻO ka porosity haʻahaʻa, ke kūpaʻa kemika kiʻekiʻe, ka hana wela kiʻekiʻe, ke kūpaʻa ʻaʻahu kiʻekiʻe

Nā ʻike kikoʻī

Hoʻohana pinepine ʻia ka huahana e like me nā mea kiln like ʻole no ka metallurgy, petrochemical, petroleum, mīkini, nā mea kūkulu hale a me nā ʻoihana ʻē aʻe.

Kiʻekiʻe Alumina Cement CA-50

Nā mea			Unite	A600	A700	G9
haku mele ʻana	Al₂O₃		%	50-60	50-60	53.5max
	CaO		%	33 min	33.00 min	33.00 min
	SiO₂		%	8.00 ka nui	8.00 ka nui	5.50 ka nui
	Fe₂O₃		%	2.50 ka nui	2.50 ka nui	2.50 ka nui
	RO₂		%	0.4max	0.40 ka nui	0.40 ka nui
Ili Aea			cm³/g	3000 ka nui	3000 ka nui	350 min
Hoʻomaka ʻia			min	60 min	60 min	90 min
Hoʻopau Hoʻonohonoho			h	6max	6max	6 min
Kulou ikaika		1 lā	Mpa	5.50 ka nui	7.00 min	8.00 min
Kulou ikaika		3 lā	Mpa	6.50 ka nui	8.00 min	10.00 min
Ka ikaika hoʻopili		1 lā	Mpa	40.00 ka nui	50.00 min	72.00 min
Ka ikaika hoʻopili		3 lā	Mpa	50.00 ka nui	60.00 min	82.00 min
Nā mea hoʻopaʻa			℃	1350	1350	1450

ʻO ka Sima Alumina Calcium

Nā mea			Unite	CA-70	CA-80
haku mele ʻana	Al₂O₃		%	68.50-72.00	78.50-81.00
	CaO		%	28.0-31.50	17.00-20.00
	SiO₂		%	≤0.50	≤0.40
	Fe₂O₃		%	≤0.50	≤0.30
	K₂O+Na₂O		%	≤0.50
Ili Aea			Cm²/g	≥5000	≥7000
Hoʻomaka ʻia			min	≥45	≥30
Hoʻopau Hoʻonohonoho			h	≤6	≤6
Kulou ikaika		24h	Mpa	≥7.0	≥5.50
Hoʻopiʻi Ka ikaika		24h	Mpa	≥45	≥40
Nā mea hoʻopaʻa			℃	≥1600	≥1790